The use of nanoparticle-in-matrix composites is a common motif among a broad range of nanoscience applications and is of particular interest to the thermal sciences community. To explore this morphological theme, crystalline inorganic composites were synthesized by mixing colloidal CdSe nanocrystals and In2Se3 metal chalcogenide complex (MCC) precursor in hydrazine solvent and then thermally transform the MCC precursor into a crystalline In2Se3 matrix. The volume fraction of CdSe nanocrystals was varied from 0 to ~100% .Rich structural and chemical interactions between the CdSe nanocrystals and the In2Se3 matrix were observed. The average thermal conductivities of the 100% In2Se3 and ~100% CdSe composites are 0.32 and 0.53 W/m-K, respectively, which are remarkably low for inorganic crystalline materials. With the exception of the ~100% CdSe samples, the thermal conductivities of these nanocomposites are insensitive to CdSe volume fraction.This insensitivity is attributed to competing effects rise from structural morphology changes during composite formation.

Next, thermoelectric properties of metal chalcogenide thin films deposited from precursors using thiol-amine solvent mixtures were first reported. Cu2-xSeyS1-y and Ag-doped Cu2-xSeyS1-y thin films were synthesized, and the interrelationship between structure, composition, and room temperature thermoelectric properties was studied. The precursor annealing temperature affects the metal:chalcogen ratio, and leads to charge carrier concentration changes that affect Seebeck coefficient and electrical conductivity. Incorporating Ag into the Cu2-xSeyS1-y film leads to appreciable improvements in thermoelectric performance. Overall, the room temperature thermoelectric properties of these solution-processed materials are comparable to measurements on Cu2-xSe alloys made via conventional thermoelectric material processing methods.

Finally, a new route to make soluble metal chalcogenide precursors by reacting organic dichalcogenides with metal in different solvents was reported. By this method, SnSe, PbSe, SnTe and PbSexTe1-x precursors were successfully synthesized, and phase-pure and impurity-free metal chalcogenides were recovered after precursor decomposition. Compared to the hydrazine and diamine-dithiol route, the new approach uses safe solvent, and avoids introducing unwanted sulfur into the precursor. SnSe and PbSexTe1-x thin films, both of which are interesting thermoelectric materials, were also successfully made by solution deposition. The thermoelectric property measurements on those thin films show a great potential for future improvements.