This research work demonstrates the process feasibility of Ultrasonic Filament Modeling process as a metal additive manufacturing process. Additive manufacturing (or 3d printing) is the method to manufacture 3d objects layer by layer. Current direct or indirect metal additive manufacturing processes either require a high power heat source like a laser or an electron beam, or require some kind of a post processing operation to produce net-shape fully-dense 3D components. The novel process of Ultrasonic Filament Modeling uses ultrasonic energy to achieve voxel deformation and inter-layer and intra-layer mass transport between voxels causing metallurgical bonding between the voxels. This enables the process to build net-shape 3D components at room temperature and ambient conditions. Two parallel mechanisms, ultrasonic softening and enhanced mass transport due to ultrasonic irradiation enable the voxel shaping and bonding respectively. This work investigates ultrasonic softening and the mass transport across voxels. Microstructural changes in aluminium during the voxel shaping have also been investigated. The temperature evolution during the process has been analyzed and presented in this work.

In this research work, the process optimization of silver iodide-silver meta phosphate ionic glass molding for solid state super ionic stamping was performed. Solid state super ionic stamping is a process of all solid ambient condition electrochemical nano patterning technique. In solid state super ionic stamping, anodic dissolution on a solid electrolyte –metal interface and subsequent charge-mass transport in the solid electrolyte is used for obtaining nanometer features on the metallic surface. The solid electrolyte referred to as the stamp is pre-patterned with features to be obtained on the metallic surface. This research developed the process for obtaining stamp with specific dimensions by making use of compression molding. The compression molding process was optimized by varying the five process parameters-temperature, pressure, holding time, pressing time and cooling time. The objective of the process optimization was to obtain best geometrical features for the stamp including flatness and surface roughness and by optimizing the compression molding process, stamp with minimum flatness and surface roughness was obtained. After the experimental optimization of the process was completed, statistical analysis was performed to understand the relative significance of the process parameters and the interaction of the process parameters on the flatness and surface roughness values of the molded stamp. Structural characterization was performed to obtain the variation of average domain size of ionic glass particles within the molded glass disk by varying the process parameters of holding time, pressing time and cooling time.