The (110) plane of Co₃O₄ spinel exhibits significantly higher rates of carbon monoxide conversion due to the presence of active Co³⁺ species at the surface. However, experimental studies of Co₃O₄ (110) surfaces and interfaces have been limited by the difficulties in growing high-quality films. We report thin (10–250 Å) Co₃O₄ films grown by molecular beam epitaxy in the polar (110) direction on MgAl₂O₄ substrates. Reflection high-energy electron diffraction, atomic force microscopy, x-ray diffraction, and transmission electron microscopy measurements attest to the high quality of the as-grown films. Furthermore, we investigate the electronic structure of this material by core level and valence band x-ray photoelectron spectroscopy, and first-principles density functional theory calculations. Ellipsometry reveals a direct band gap of 0.75 eV and other interband transitions at higher energies. A valence band offset of 3.2 eV is measured for the Co₃O₄/MgAl₂O₄ heterostructure. Magnetic measurements show the signature of antiferromagnetic ordering at 49 K. FTIR ellipsometry finds three infrared-active phonons between 300 and 700 cm^-1.

Zintl phases are a class of intermetallic materials that have simultaneously ionic and covalent bonding resulting from charge transfer between two different atomic species. We present a combined first principles and experimental study of Zintl-phase SrAl4, which is grown in thin film form on the perovskite oxide LaAlO3 using molecular beam epitaxy. The structural properties are investigated using reflection-high-energy electron diffraction, x-ray diffraction, and cross-section transmission electron microscopy, which reveal relaxed epitaxial island growth. Photoelectron spectroscopy measurements verify the Zintl-Klemm nature of the bonding in the material and are utilized to determine the band offset and the work function of SrAl4, while transport measurements confirm its metallic behavior. The experimentally observed properties are confirmed using density functional calculations.