In this paper, we report on the highly conductive layer formed at the crystalline γ-alumina/SrTiO₃ interface, which is attributed to oxygen vacancies. We describe the structure of thin γ-alumina layers deposited by molecular beam epitaxy on SrTiO3 (001) at growth temperatures in the range of 400–800 °C, as determined by reflection-high-energy electron diffraction, x-ray diffraction, and high-resolution electron microscopy. In situ x-ray photoelectron spectroscopy was used to confirm the presence of the oxygen-deficient layer. Electrical characterization indicates sheet carrier densities of ∼1013 cm−2 at room temperature for the sample deposited at 700 °C, with a maximum electron Hall mobility of 3100 cm²V^-1s^-1 at 3.2 K and room temperature mobility of 22 cm²V^-1s^-1. Annealing in oxygen is found to reduce the carrier density and turn a conductive sample into an insulator.

The (110) plane of Co₃O₄ spinel exhibits significantly higher rates of carbon monoxide conversion due to the presence of active Co³⁺ species at the surface. However, experimental studies of Co₃O₄ (110) surfaces and interfaces have been limited by the difficulties in growing high-quality films. We report thin (10–250 Å) Co₃O₄ films grown by molecular beam epitaxy in the polar (110) direction on MgAl₂O₄ substrates. Reflection high-energy electron diffraction, atomic force microscopy, x-ray diffraction, and transmission electron microscopy measurements attest to the high quality of the as-grown films. Furthermore, we investigate the electronic structure of this material by core level and valence band x-ray photoelectron spectroscopy, and first-principles density functional theory calculations. Ellipsometry reveals a direct band gap of 0.75 eV and other interband transitions at higher energies. A valence band offset of 3.2 eV is measured for the Co₃O₄/MgAl₂O₄ heterostructure. Magnetic measurements show the signature of antiferromagnetic ordering at 49 K. FTIR ellipsometry finds three infrared-active phonons between 300 and 700 cm^-1.