Zeolite thin films and membranes are currently a promising technology for pervaporation, gas separation and water purification. The main drawback with these technologies is that the synthesis is not consistent leading to varied and unreproducible results. The Langmuir-Blodgett technique is a robust method for transferring monolayers of molecules or crystals to a solid substrate. By measuring the surface pressure and controlling the area, reliable results can be achieved by transferring monolayers to different solid substrates. It has been shown previously that various types of zeolites can be functionalized and dispersed on the top of water. This is done by using an alcohol to form a hydrophobic coating on the surface of zeolite. The Langmuir-Blodgett can be used to create thin, compact films of zeolites for synthesizing and growing zeolite films. For the first reported time, cubic LTA Zeolites monolayers have been assembled with the Langmuir-Blodgett technique with multiple solvents and different sizes of zeolites. These films were characterized with Scanning Electron Microscopy and Pressure-Area Isotherms generated from the Langmuir-Blodgett. It was found that linoleic acid is a required addition to the zeolite dispersions to protect the mechanical stability during agitation. Without this addition, the LTA zeolites are broken apart and lose their characteristic cubic structure. This effect is discussed and a theory is presented that the interparticle interactions of the long alkane chain of the linoleic acid help reduce the shear stress on the individual zeolite particles, thus preventing them from being broken. The effect of size of the zeolites on the monolayer formation was also discussed. There seemed to be little correlation between the monolayer quality and formation as size was changed. However, to optimize the process, different concentrations and target pressures are needed. Lastly, the effect of the solvent was explored and it was found that there is a different between monolayer formations for different solvents likely due to differing interparticle interactions. Overall, LTA zeolites were successfully fabricated and the important factors to consider are the zeolite size, the solvent, and the amount of surfactant stabilizer added.

The overall goal of this project is to use metallic nanoparticles to develop a thin, ductile amorphous film at room temperature. Currently bulk metallic glasses are mainly formed via quenching, which requires very high cooling rates to achieve an amorphous molecular structure. These formations often fail in a brittle manner. The advantages of using a bottom-up approach with amorphous nanoparticles at ambient conditions is that the ductility of the metal can be improved, and the process will be less energy intensive. The nanoparticles used are iron precursors with ATMP and DTPMP ligand stabilizers and dispersed in methanol. Three forms of experimentation were applied over the course of this project. The first was a simple, preliminary data collection approach where the particles were dispersed onto a glass slide and left to dry under various conditions. The second method was hypersonic particle deposition, which accelerated the particles to high speeds and bombarded onto a glass or silicon substrate. The third method used Langmuir-Blodgett concepts and equipment to make a film. Qualitative analyses were used to determine the efficacy of each approach, including SEM imaging. In the end, none of the approaches proved successful. The first approach showed inconsistencies in the film formation and aggregation of the particles. The results from the hypersonic particle deposition technique showed that not enough particles were deposited to make a consistent film, and many of the particles that were able to be deposited were aggregated. The Langmuir-Blodgett method showed potential, but aggregation of the particles and uneven film formation were challenges here as well. Although there are ways the three discussed experimental approaches could be optimized, the next best step is to try completely new approaches, such as convective assembly and 3D printing to form the ideal nanoparticle film.