Strategies to Enhance the Charge Dynamics of Bismuth Vanadate For Photocatalytic Water Oxidation

Hydrogen is considered one of the most potential fuels due to its highest gravimetric energy density with no pollutant emission during the energy cycle. Among several techniques for hydrogen generation, the promising photoelectrochemical water oxidation is considered a long-term solar pathway by splitting water. The system contains a photoanode and a cathode immersed in an aqueous electrolyte where charge separation takes place in the bulk of the semiconducting material on light absorption, leading to water oxidation/reduction at the surface of the photoelectrodes/cathode. It is imperative to develop materials that demonstrate high light absorption in the wide spectrum along with photoelectrochemical stability. N-type Monoclinic scheelite bismuth vanadate (BiVO4) is selected due to its incredible light absorption capabilities, direct bandgap (Eg ∼ 2.4-2.5 eV) and relatively better photoelectrochemical stability. However, BiVO4 encounters huge electron-hole recombination due to smaller diffusion lengths and positive conduction bands that cause slow charge dynamics and sluggish water oxidation kinetics. In order to improve the illustrated drawbacks, four strategies were discussed. Chapter 1 describe the fundamental understanding of photoelectrochemical cell and BiVO4. Chapter 2 illustrates details of the experimental procedure and state-of-the-art material characterization. Chapter 3 provide the impact of alkali metal placement in the crystal structure of BiVO4 systematically that exhibited ~20 times more performance than intrinsic BiVO4, almost complete bulk charge separation and enhancement in the diffusion length. Detailed characterization determined that the alkali metal getting placed in the interstitial void of BiVO4 lattice and multiple interbands formation enhanced the charge dynamics. Chapter 4 contains stoichiometric doping of Y3+ or Er3+ or Yb3+ at the Bi3+ site, leading to an extended absorption region, whereas non-stoichiometric W6+ doping at the V5+ site minimizes defects and increased charge carriers. To further enhance the performance, type-II heterojunction with WO3 along p-n junction with Fe:NiO enhance light absorption and charge dynamics close to the theoretical performance. Chapter 5 provides a comprehensive study of a uniquely developed sulfur modified Bi2O3 interface layer to facilitate charge dynamics and carrier lifetime improvement by effectively passivating the WO3/BiVO4 heterojunction interface. Finally, chapter 6 summarized the major findings, conclusion and outlook in developing BiVO4 as an efficient photoanode material.