This dissertation will investigate two of the most promising high-capacity anode
materials for lithium-based batteries: silicon (Si) and metal lithium (Li). It will focus on
studying the mechanical behaviors of the two materials during charge and discharge and
understanding how these mechanical behaviors may affect their electrochemical
performance.
In the first part, amorphous Si anode will be studied. Despite many existing studies
on silicon (Si) anodes for lithium ion batteries (LIBs), many essential questions still exist
on compound formation, composition, and properties. Here it is shown that some
previously accepted findings do not truthfully reflect the actual lithiation mechanisms in
realistic battery configurations. Furthermore the correlation between structure and
mechanical properties in these materials has not been properly established. Here, a rigorous
and thorough study is performed to comprehensively understand the electrochemical
reaction mechanisms of amorphous-Si (a-Si) in a realistic LIB configuration. In-depth
microstructural characterization was performed and correlations were established between
Li-Si composition, volumetric expansion, and modulus/hardness. It is found that the
lithiation process of a-Si in a real battery setup is a single-phase reaction rather than the
accepted two-phase reaction obtained from in-situ TEM experiments. The findings in this
dissertation establish a reference to quantitatively explain many key metrics for lithiated a
Si as anodes in real LIBs, and can be used to rationally design a-Si based high-performance
LIBs guided by high-fidelity modeling and simulations.
In the second part, Li metal anode will be investigated. Problems related to dendrite
growth on lithium metal anodes such as capacity loss and short circuit present major
barriers to the next-generation high-energy-density batteries. The development of
successful mitigation strategies is impeded by the incomplete understanding of the Li
dendrite growth mechanisms. Here the enabling role of plating residual stress in dendrite
initiation through novel experiments of Li electrodeposition on soft substrates is confirmed,
and the observations is explained with a stress-driven dendrite growth model. Dendrite
growth is mitigated on such soft substrates through surface-wrinkling-induced stress
relaxation in deposited Li film. It is demonstrated that this new dendrite mitigation
mechanism can be utilized synergistically with other existing approaches in the form of
three-dimensional (3D) soft scaffolds for Li plating, which achieves superior coulombic
efficiency over conventional hard copper current collectors under large current density.
materials for lithium-based batteries: silicon (Si) and metal lithium (Li). It will focus on
studying the mechanical behaviors of the two materials during charge and discharge and
understanding how these mechanical behaviors may affect their electrochemical
performance.
In the first part, amorphous Si anode will be studied. Despite many existing studies
on silicon (Si) anodes for lithium ion batteries (LIBs), many essential questions still exist
on compound formation, composition, and properties. Here it is shown that some
previously accepted findings do not truthfully reflect the actual lithiation mechanisms in
realistic battery configurations. Furthermore the correlation between structure and
mechanical properties in these materials has not been properly established. Here, a rigorous
and thorough study is performed to comprehensively understand the electrochemical
reaction mechanisms of amorphous-Si (a-Si) in a realistic LIB configuration. In-depth
microstructural characterization was performed and correlations were established between
Li-Si composition, volumetric expansion, and modulus/hardness. It is found that the
lithiation process of a-Si in a real battery setup is a single-phase reaction rather than the
accepted two-phase reaction obtained from in-situ TEM experiments. The findings in this
dissertation establish a reference to quantitatively explain many key metrics for lithiated a
Si as anodes in real LIBs, and can be used to rationally design a-Si based high-performance
LIBs guided by high-fidelity modeling and simulations.
In the second part, Li metal anode will be investigated. Problems related to dendrite
growth on lithium metal anodes such as capacity loss and short circuit present major
barriers to the next-generation high-energy-density batteries. The development of
successful mitigation strategies is impeded by the incomplete understanding of the Li
dendrite growth mechanisms. Here the enabling role of plating residual stress in dendrite
initiation through novel experiments of Li electrodeposition on soft substrates is confirmed,
and the observations is explained with a stress-driven dendrite growth model. Dendrite
growth is mitigated on such soft substrates through surface-wrinkling-induced stress
relaxation in deposited Li film. It is demonstrated that this new dendrite mitigation
mechanism can be utilized synergistically with other existing approaches in the form of
three-dimensional (3D) soft scaffolds for Li plating, which achieves superior coulombic
efficiency over conventional hard copper current collectors under large current density.
Download count: 5
Details
Title
- Understanding the Mechanical Behaviors of Lithium-Based Battery Anodes─Silicon and Lithium Metal
Contributors
- Wang, Xu (Author)
- Jiang, Hanqing (Thesis advisor)
- Yu, Hongbin (Thesis advisor)
- Chan, Candace (Committee member)
- Wang, Liping (Committee member)
- Qiong, Nian (Committee member)
- Arizona State University (Publisher)
Date Created
The date the item was original created (prior to any relationship with the ASU Digital Repositories.)
2018
Subjects
Resource Type
Collections this item is in
Note
-
Doctoral Dissertation Mechanical Engineering 2018