Selenium removal from power plant waste water with solid phase extraction materials

As selenium is toxic at low levels, treatment methods to remove selenium from industrial waste waters are needed. In this work, three groups of sorbent materials were investigated in detail for their effectiveness for selenium and arsenic removal from water: 1) nanostructured carbon-based materials, 2) layered double hydroxide (LDH)-based materials, and 3) biopolymer-based sorbents. The materials were investigated in spiked de-ionized water and waters collected from different locations at Salt River Project’s (SRP) Santan Generating Station in Gilbert, AZ. The results show that nanostructured carbon-based materials removed ~80% and up to 100% selenium and arsenic, respectively in spiked DI water. Heat treated layered double hydroxides removed close to 100% removal in selenium and arsenic spiked DI water. Isotherms conducted in spiked DI water fit the Langmuir model and showed a maximum selenate adsorption capacity of 67 mg/g for the calcined LDH powder. Results from SRP waters showed that certain LDH sorbents were effective for removing the selenium, but that higher pH and existence of competing ions affected the removal efficiencies. The functionalized biopolymer sorbent from Crystal Clear Technologies: CCT-149/OCI-B showed good removal efficiencies for both selenate and selenite in DI water. Isotherms conducted in spiked DI water for CCT-149 fit the Langmuir model and showed a maximum selenate adsorption capacity of 90.9 mg/g. Column tests using spiked DI water and waters obtained from SRP wells were investigated using both LDH and CCT-149/OCI-B. Removal of sulfate using chemical pre-treatment of the water with barium chloride resulted in about three times higher selenate loading onto the granular LDH and doubled the water volume that can be treated using CCT-149/OCI-B. The results from the column tests are being used to guide the pilot testing investigating the implementation of LDH sorbents at pilot scale at the Santan plant. The good results in the cooling tower #5 blowdown water and combined discharge waste water of SRP provide valuable information about the efficacy and efficiency of adsorptive media for the removal of selenium. Composites comprising LDH nanosheets with different substrates were successfully synthesized that were able to retain the performance in removing selenate of nanosheet LDH.