Ionic Liquids to Lab: Investigating an Emerging Water Filtration Challenge to Engineering Nanofiber Polymer Membranes as Next-Generation Solutions for Water Purification

The following thesis documents a two-fold approach to investigate challenges pertaining to water purification, first through a meta-analysis of ionic liquid toxicity, then through experimentation aimed at developing water pre-treatment membranes. Ionic liquids (ILs) are salts with low melting points, typically liquid at room temperature. Several extraordinary physical attributes, e.g. low viscosity, high conductivity, low to no vapor pressure, etc., and seemingly unlimited combinations available, have pushed IL research to the forefront of many research fronts. Concerns are raised as ionic liquids are rushed into commercial production without sufficient environmental regulation. Research has shown that the chemicals are in fact toxic, yet have developed a reputation for being “green” chemicals due to select physical attributes and applications. The meta-analysis discussed focuses on industry perception of ionic liquid toxicity through a patent review, and considers toxicity of ILs comparatively against other chemical families with well-established toxicity. The meta-analysis revealed that the total patent literature pertaining to ILs (n=3358) resulted in 112 patents that addressed the toxicity of ILs, and notably few (n=17) patents defined ILs as toxic, representing only 0.51% of the evaluated body of work on intellectual property claims. Additionally, toxicity of ionic liquids is comparable to that of other chemical families.
The objective of the experimentation was to explore the effect of crosslinker chain length on the morphology of nanofiber mats. Specifically, poly(vinyl alcohol (PVA) was electrospun into nanofiber mats and poly(ethylene) glycol bis(carboxylic acid) (PEG diacid) was used as the crosslinking agent. As-spun fibers had average fiber diameter of 70 ± 30 nm with an average pore size of 0.10 ± 0.16 μm^2. The fiber diameter for the mats crosslinked with the shorter PEG diacid (Mn = 250) increased to 110 ± 40 nm with an average pore size of 0.11 ± 0.04 μm^2. The mats crosslinked with the longer PEG diacid (Mn = 600) had fiber diameters of 180 ± 10 nm with an average pore size 0.01 ± 0.02 μm^2.